Product Details:
Brand | Akfix |
Hardness | 55-60 Shore A (After 28 days) |
Density | 1,13+-0,03 g/ml |
Curing Rate | Min. 3,5 mm/day (23 deg C and 50% R.H) |
Elongation At Break | Min. 300% |
Basis | Polyurethane |
Consistency | Thixotropic |
Curing Mechanism | Moisture Curing |
Tack Free Time | 30+-10 min. (23 deg C and 50% R.H) |
Sagging | 0 mm |
Paintibility | Yes |
Tensile Strength | Min. 4 N/mm 2 |
Polyurethane Windshield Adhesive is a component, moisture curing polyurethane based adhesive for direct glazing in Automotive Glass Replacement.
Properties:
It is especially useful in bonding windshield glass into automotive frames
Product Details:
Brand | Akfix |
Density | 1,70 + 0,03 g/ml |
Curing Rate | 1 - 2 mm/day |
Application | Tyre Repair |
Product Details:
Brand | Akfix |
Form | Liquid Aerosol |
Shelf Life | 24 months (20 deg C) |
Volume | 500ml |
Box Quantity | 12 Piece |
Appearance | White Foam |
Density | 0,928 g/cm 3 |
Odor | Characteristic |
pH | 8-9 |
Specially developed for cleaning, treating and protecting tyres as well as enhancing their appearance in one process. Enhances the appearance of weathered tires by restoring the rubber surface
Properties:
Akfix Tyre Cleaner & Polish Foam is suitable to use on all kind of vehicle tires like bicycles, motorcycles, automobiles, minibuses, buses, trucks, lorries etc.
Additional Information:
Product Details:
Packaging Type | Can |
Brand | Akfix |
Form | Liquid Aerosol |
Appearance | Transparent |
Specific Gravity | 0,72+-0,02 gr/cm 3 |
Odor | Characteristic |
Flash Point | N/A |
Volume | 500ml |
Box Quantity | 24 Piece |
Powerful cleaning aerosol is used to remove oil, grease, dirt and dust from brakes and clutches, aiding in the elimination of brake squeal and clutch slip caused by glazing and contamination. Brake c
Properties:
Perfect for cleaning and degreasing:
Additional Information:
Product Details:
Brand | Akfix |
Form | Aerosol |
Appearance | Transparent |
Specific Gravity | 1 gr/cm 3 |
Odor | Characteristic |
Flash Point | N/A |
Solid Content | 50% |
Volume | 300ml |
Box Quantity | 24 Piece |
Eliminates the need for an immediate tyre change, sealing and inflating your tyre within seconds.
Properties:
Additional Information:
Product Details:
Packaging Type | Can |
Brand | Akfix |
Color | Clear |
Form | Aerosol |
Odor | Light Citrus |
Specific Gravity | 0,758 g/cm3 |
Volume | 500ml |
Box Quantity | 24 Piece |
A115 Engine Cleaner Spray is an excellent product developed against engine oil, grease and stubborn dirt.
Properties:
Additional Information:
Product Details:
Brand | Akfix |
Temperature Resistance | -40 deg C to +300 deg C |
Basis | Silicone Polymer |
Elongation At Break | 250% |
Elastic Recovery | 60% |
Sagging | 0 mm |
Application Temperature | +5 deg C to +40 deg C |
Curing System | Acetoxy |
Density | 1.05+- 0.03 g/ml |
Hardness Shore A | 24-30 (after 28 days) |
Tensile Strength | 1,5 N/mm 2 (23 deg C and 50% R.H) |
Skin Formation | 7-13 min. (23 deg C and 50% R.H) |
Curing Rate | Min. 3 mm/day (23 deg C and 50% R.H) |
Akfix HT300 is a high-performance silicone sealant developed for sealing, bonding and repairing works where heat resistance is required. It is an ideal sealant for high temperature construction applications. It reacts with atmospheric moisture to produce a tough, elastic silicone.
Properties:
Additional Information:
Product Details:
Brand | Akfix |
Color | Black |
Application Temperature | +10 deg C to +35 deg C |
Appearance | Liquid |
Specific Gravity | 0,95 gr/cc |
Odour | Characteristic of Solvent |
Curing Mechanism | Moisture-Curing |
Minimum Drying Time | 3' at 23 deg C and 50% r.h |
Maximum Drying Time | 24h at 23 deg C and 50% r.h |
Volume | 250 ml |
Box Quantity | 12 Bottles Per Box |
Polyurethane Windshield Adhesive Primer is a BLACK Primer specifically designed for the ceramic band on vehicle glass. It ensures the complete protection of the adhesive by creating a barrier against harmful UV rays which can lead to the degradation of the adhesive. It is also an adhesion promoter. To be used in conjunction with Cleaner/Activator.
Properties:
The surfaces to be treated must be perfectly clean, dry, dust and grease free. Application of Polyurethane Windshield Adhesive Primer can only take place once the thorough cleaning of the bonding area with CLEANER/ACTIVATOR has been completed. Shake bottle well before application (for at least 1 min.) till the noise of the metal balls contained in the bottle can be heard. Apply product using a felt applicator. Close immediately after use as product evaporates very quickly. Ensure that primer is tack-free dry before proceeding.
Product Details:
Brand | Akfix |
Glue Basis | Ethyl Cyanoacrylate |
Activator Appearance | Aerosol |
Activator Color | Colorless |
Activator Application Temperature | +5 deg C to +35 deg C |
Activator Temperature Resistance | -20 deg C to +70 deg C |
Glue Appearance | Liquid gel |
Glue Color | Colorless |
Glue Application Temperature | +5 deg C to +35 deg C |
Density | 1.06 +- 0.01 gr/cm 3 |
Flashpoint | 81 deg C |
Viscosity | 1200 - 1800 Cps at 25 deg C |
Temperature Resistance | -20 deg C to +70 deg C |
Activator Basis | Hexane |
Auto Kit is a two part special set consist of a high viscosity cyanoacrylate adhesive and activator set which is used especially on wood, rubber, most plastics, small glass piec e s, leather and other common substrates in the auto mobile.
Properties:
Additional Information:
Product Details:
Brand | Akfix |
Chemical Base | MS Polymer |
Volume Loss | -%3 (23 deg C and %50 R.H.) |
Tensile Strength | 3,0-3,5 N/mm 2 |
Heat Resistance | -40 deg C and +90 deg C |
Application Temperature | +5 deg C and +40 deg C |
Volume | 290 ml,600ml |
Box Quantity | 12 Piece |
Curing System | Moisture |
Density | 1.49 +- 0.03 gr/ml |
Appearance or Color | Paste,White,Black or Grey |
Tack Free | 15-20 min (23 deg Cand %50 R.H.) |
Curing Rate | Approx. 3,5 mm/ 24 hr (23 deg Cand %50 R.H.) |
Sagging | 0 mm |
Shore A Hardness | 55 +-5 |
Elongation at Break | % 300 |
MS Polymer Windshield Adhesive is an isocyanate-free, thixotropic, high modulus, primerless windshield adhesive based on MS Polymer technology. It provides quick drive-away time and easy application without pre-heating for vehicles.
Properties: